Standard Specification for Titanium and Titanium Alloy Wire

PUBLISH DATE 2026
PAGES 7
ASTM B863-26

This specification covers titanium and titanium alloy wire.

The chemical composition; physical properties such as density; and mechanical properties such as tensile strength, elongation, and hardness are detailed.

1.1 This specification covers titanium and titanium alloy wire as follows:

  • 1.1.1 Grade 1—UNS R50250. Unalloyed titanium,
  • 1.1.2 Grade 2—UNS R50400. Unalloyed titanium,
    • 1.1.2.1 Grade 2H—UNS R50400. Unalloyed titanium (Grade 2 with 58 ksi (400 MPa) minimum UTS),
  • 1.1.3 Grade 3—UNS R50550. Unalloyed titanium,
  • 1.1.4 Grade 4—UNS R50700. Unalloyed titanium,
  • 1.1.5 Grade 5—UNS R56400. Titanium alloy (6 % aluminum, 4 % vanadium),
  • 1.1.6 Grade 6—UNS R54520. Titanium alloy (5 % aluminum, 2.5 % tin),
  • 1.1.7 Grade 7—UNS R52400. Unalloyed titanium plus 0.12 % to 0.25 % palladium,
    • 1.1.7.1 Grade 7H—UNS R52400. Unalloyed titanium plus 0.12 % to 0.25 % palladium (Grade 7 with 58 ksi (400 MPa) minimum UTS),
  • 1.1.8 Grade 9—UNS R56320. Titanium alloy (3 % aluminum, 2.5 % vanadium),
  • 1.1.9 Grade 11—UNS R52250. Unalloyed titanium plus 0.12 % to 0.25 % palladium,
  • 1.1.10 Grade 12—UNS R53400. Titanium alloy (0.3 % molybdenum, 0.8 % nickel),
  • 1.1.11 Grade 13—UNS R53413. Titanium alloy (0.5 % nickel, 0.05 % ruthenium),
  • 1.1.12 Grade 14—UNS R53414. Titanium alloy (0.5 % nickel, 0.05 % ruthenium),
  • 1.1.13 Grade 15—UNS R53415. Titanium alloy (0.5 % nickel, 0.05 % ruthenium),
  • 1.1.14 Grade 16—UNS R52402. Unalloyed titanium plus 0.04 % to 0.08 % palladium,
    • 1.1.14.1 Grade 16H—UNS R52402. Unalloyed titanium plus 0.04 % to 0.08 % palladium (Grade 16 with 58 ksi (400 MPa) minimum UTS),
  • 1.1.15 Grade 17—UNS R52252. Unalloyed titanium plus 0.04 % to 0.08 % palladium,
  • 1.1.16 Grade 18—UNS R56322. Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.04 % to 0.08 % palladium,
  • 1.1.17 Grade 19—UNS R58640. Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 % molybdenum),
  • 1.1.18 Grade 20—UNS R58645. Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 % molybdenum) plus 0.04 % to 0.08 % palladium,
  • 1.1.19 Grade 21—UNS R58210. Titanium alloy (15 % molybdenum, 3 % aluminum, 2.7 % niobium, 0.25 % silicon),
  • 1.1.20 Grade 23—UNS R56407. Titanium alloy (6 % aluminum, 4 % vanadium with extra low interstitial elements, ELI),
  • 1.1.21 Grade 24—UNS R56405. Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.04 % to 0.08 % palladium,
  • 1.1.22 Grade 25—UNS R56403. Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.3 % to 0.8 % nickel and 0.04 % to 0.08 % palladium,
  • 1.1.23 Grade 26—UNS R52404. Unalloyed titanium plus 0.08 % to 0.14 % ruthenium,
    • 1.1.23.1 Grade 26H—UNS R52404. Unalloyed titanium plus 0.08 % to 0.14 % ruthenium (Grade 26 with 58 ksi (400 MPa) minimum UTS),
  • 1.1.24 Grade 27—UNS R52254. Unalloyed titanium plus 0.08 % to 0.14 % ruthenium,
  • 1.1.25 Grade 28—UNS R56323. Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.08 % to 0.14 % ruthenium,
  • 1.1.26 Grade 29—UNS R56404. Titanium alloy (6 % aluminum, 4 % vanadium with extra low interstitial elements, ELI) plus 0.08 % to 0.14 % ruthenium,
  • 1.1.27 Grade 32—UNS R55111. Titanium alloy (5 % aluminum, 1 % tin, 1 % vanadium, 1 % zirconium, 0.8 % molybdenum),
  • 1.1.28 Grade 33—UNS R53442. Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),
  • 1.1.29 Grade 34—UNS R53445. Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),
SDO ASTM: ASTM International
Document Number B863
Publication Date April 1, 2026
Language en - English
Page Count 7
Revision Level 26
Supercedes
Committee B10.01
Loading...

Failed to load document history.

Publish Date Document Id Type View