| SAE |
SAE AMS4784 |
Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range
|
|
| SAE |
SAE AMS4782 |
Nickel Alloy, Brazing Filler Metal 71Ni - 10Si - 19Cr 1975 °F (1080 °C) Solidus, 2075 °F (1135 °C) Liquidus
|
|
| SAE |
SAE AMS4787 |
Gold-Nickel Alloy, Brazing Filler Metal, High Temperature 82Au - 18Ni 1740 °F (949 °C) Solidus-Liquidus Temperature
|
|
| SAE |
SAE AMS4786 |
Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range
|
|
| SAE |
SAE AMS4775 |
Nickel Alloy, Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus
|
|
| SAE |
SAE AMS4779 |
Nickel Alloy, Brazing Filler Metal 94Ni - 3.5Si - 1.8B 1800 °F (982 °C) Solidus, 1950 °F (1066 °C) Liquidus
|
|
| SAE |
SAE AMS4777 |
Nickel Alloy, Brazing Filler Metal 82Ni - 4.5Si - 7.0Cr - 3.1B - 3.0Fe 1780 °F (971 °C) Solidus to 1830 °F (999 °C) Liquidus Range
|
|
| SAE |
SAE AMS4776 |
Nickel Alloy, Brazing Filler Metal, 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon), 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus Range
|
|
| SAE |
SAE AMS4783 |
Cobalt Alloy, High Temperature Brazing Filler Metal 50Co - 8.0Si - 19Cr - 17Ni - 4.0W - 0.80B 2050 to 2100 °F (1121 to 1149 °C) Solidus-Liquidus Range
|
|
| BSI |
BSI BS A 317 |
Nuts, hexagonal, plain, normal height, normal across flats, with MJ threads, classifications. 600 MPa (at ambient temperature)/120°C, 600 MPa (at ambient temperature)/235°C, 900 MPa (at ambient temperature)/425°C, 1100 MPa (at ambient temperature)/235°C, 1100 MPa (at ambient temperature)/315°C, 1100 MPa (at ambient temperature)/650°C, 1210 MPa (at ambient temperature)/730°C, 1250 MPa (at ambient temperature)/235°C and 1550 MPa (at ambient temperature)/600°C. Dimensions |
|
| BSI |
BSI BS ISO 9618 |
Aerospace. Nuts, hexagonal, slotted (castellated), reduced height, normal across flats, with MJ threads, classifications: 450 MPa (at ambient temperature)/120 °C, 450 MPa (at ambient temperature)/235 °C, 600 MPa (at ambient temperature)/425 °C, 900 MPa (at ambient temperature)/235 °C, 900 MPa (at ambient temperature)/315 °C, 900 MPa (at ambient temperature)/650 °C, 1 100 MPa (at ambient temperature)/235 °C, 1 100 MPa (at ambient temperature)/730 °C and 1 250 MPa (at ambient temperature)/600 °C. Dimensions |
|
| SAE |
SAE AMS4766 |
Silver Alloy, Brazing Filler Metal 85Ag - 15Mn 1760 to 1780 °F (960 to 971 °C) Solidus-Liquidus Range
|
|
| BSI |
BSI BS A 316 |
Nuts, hexagonal, slotted (castellated), normal height, normal across flats, with MJ threads, classifications. 600 MPa (at ambient temperature)/120°C, 600 MPa (at ambient temperature)/235°C, 900 MPa (at ambient temperature)/425°C, 1 100 MPa (at ambient temperature)/235°C, 1 100 MPa (at ambient temperature)/315°C, 1 100 MPa (at ambient temperature)/650°C, 1 210 MPa (at ambient temperature)/730°C, 1 250 MPa (at ambient temperature)/235°C and 1 550 MPa (at ambient temperature)/600°C. Dimensions |
|
| BSI |
BSI BS ISO 8279 |
Aerospace. Nuts, hexagonal, plain, normal height, normal across flats, with MJ threads, classifications: 600 MPa (at ambient temperature)/120 °C, 600 MPa (at ambient temperature)/235 °C, 900 MPa (at ambient temperature)/425 °C, 1 100 MPa (at ambient temperature)/235 °C, 1 100 MPa (at ambient temperature)/315 °C, 1 100 MPa (at ambient temperature)/650 °C, 1 210 MPa (at ambient temperature)/730 °C, 1 250 MPa(at ambient temperature)/235 °C and 1 550 MPa (at ambient temperature)/600 °C. Dimensions |
|
| SAE |
SAE AMS4778 |
Nickel Alloy, Brazing Filler Metal 92Ni - 4.5Si - 3.1B 1800 to 1900 °F Solidus-Liquidus Range
|
|
| SAE |
SAE MAM4778 |
Nickel Alloy, Brazing Filler Metal, 92Ni 4.5Si 3.1B, 980 to 1040°C Solidus-Liquidus Range
|
|
| SAE |
SAE AMS4762 |
Silver Alloy, Brazing Filler Metal 40Ag - 30Cu - 30Zn 1245 to 1340 °F (674 to 727 °C) Solidus-Liquidus Range
|
|
| SAE |
SAE AMS4773 |
Silver Alloy, Brazing Filler Metal 60Ag - 30Cu - 10Sn 1115 to 1325 °F (602 to 718 °C) Solidus-Liquidus Range
|
|
| SAE |
SAE AMS2663 |
Silver Alloy Brazing Filler Metal, 56Ag 22Cu 17Zn 5.0Sn, 1152 - 1203°F (622 - 651°C) Solidus-Liquidus Range
|
|
| ISO |
ISO 9618 |
Aerospace - Nuts, hexagonal, slotted (castellated), reduced height, normal across flats, with MJ threads, classifications: 450 MPa (at ambient temperature)/120 degrees C, 450 MPa (at ambient temperature)/235 degrees C, 600 MPa (at ambient temperature)/425 degrees C, 900 MPa (at ambient temperature)/235 degrees C, 900 MPa (at ambient temperature)/315 degrees C, 900 MPa (at ambient temperature)/650 degrees C, 1 100 MPa (at ambient temperature)/235 degrees C, 1 100 MPa (at ambient temperature)/730 degrees C and 1 250 MPa (at ambient temperature)/600 degrees C - Dimensions |
|
| ISO |
ISO 9609 |
Aerospace - Nuts, hexagonal, plain, reduced height, normal across flats, with MJ threads, classifications: 450 MPa (at ambient temperature) /120 degrees C, 450 MPa (at ambient temperature) /235 degrees C, 600 MPa (at ambient temperature) /425 degrees C, 900 MPa (at ambient temperature) /235 degrees C, 900 MPa (at ambient temperature) /315 degrees C, 900 MPa (at ambient temperature) /650 degrees C, 1 100 MPa (at ambient temperature) /235 degrees C, 1 100 MPa (at ambient temperature) /730 degrees C and 1 250 MPa (at ambient temperature)/600 degrees C - Dimensions |
|
| ISO |
ISO 4147 |
Aerospace - Nuts, hexagonal, slotted (castellated), normal height, normal across flats, with MJ threads, classifications: 600 MPa (at ambient temperature)/120 degrees C, 600 MPa (at ambient temperature)/235 degrees C, 900 MPa (at ambient temperature)/425 degrees C, 1 100 MPa (at ambient temperature)/235 degrees C, 1 100 MPa (at ambient temperature)/315 degrees C, 1 100 MPa (at ambient temperature)/650 degrees C, 1 210 MPa (at ambient temperature)/730 degrees C, 1 250 MPa (at ambient temperature)/235 degrees C and 1 550 MPa (at ambient temperature)/600 degrees C - Dimensions |
|
| ISO |
ISO 8279 |
Aerospace - Nuts, hexagonal, plain, normal height, normal across flats, with MJ threads, classifications: 600 MPa (at ambient temperature)/120 degrees C, 600 MPa (at ambient temperature)/235 degrees C, 900 MPa (at ambient temperature)/425 degrees C, 1 100 MPa (at ambient temperature)/235 degrees C, 1 100 MPa (at ambient temperature)/315 degrees C, 1 100 MPa (at ambient temperature)/650 degrees C, 1 210 MPa (at ambient temperature)/730 degrees C, 1 250 MPa (at ambient temperature)/235 degrees C and 1 550 MPa (at ambient temperature)/600 degrees C - Dimensions |
|
| SAE |
SAE AMS4765 |
Silver Alloy, Brazing Filler Metal 56Ag – 42Cu – 2.0Ni 1420 to 1640 °F (771 to 893 °C) Solidus-Liquidus Range
|
|
| SAE |
SAE AMS4769 |
Silver Alloy, Brazing Filler Metal 45Ag - 24Cd - 16Zn - 15Cu 1125 to 1145 °F (607 to 618 °C) Solidus-Liquidus Range
|
|